Substantial increase of the ordering temperature for [MnII/MoIII(CN)7]-based magnets as a function of the 3d ion site geometry: example of two supramolecular materials with Tc = 75 and 106 K.

Two molecule-based magnets, [Mn(2)(tea)Mo(CN)(7)].H(2)O, 1, and [Mn(2)(tea)Mo(CN)(7)], 2 (tea stands for triethanolamine), formed with the 4d ion building block, [Mo(CN)(7)](4)(-), Mn(II) ions, and an additional ligand, tea, have been prepared and structurally characterized by single-crystal X-ray analyses. Whereas 1 is obtained by a self-assembling process in solution, compound 2 is quantitatively formed through a smooth thermal treatment of 1. Their magnetic properties revealed that these compounds exhibit magnetic ordering at T(c) = 75 and 106 K respectively for compounds 1 and 2. The difference for their critical temperature is attributed to the geometry of the coordination sphere of a Mn(II) site found to be square-pyramidal for 1 and tetrahedral for 2.