Relative contributions of chemistry and topography to the osseointegration of hydroxyapatite coatings.

The purpose of the current study was to ascertain the relative contributions of surface chemistry and topography to the osseointegration of hydroxyapatite-coated implants. A canine femoral intramedullary implant model was used to compare the osseous response to commercially pure titanium implants that were either polished, grit-blasted, plasma-sprayed with hydroxyapatite, or plasma-sprayed with hydroxyapatite and masked with a very thin layer of titanium using physical vapor deposition (titanium mask). The titanium mask isolated the chemistry of the underlying hydroxyapatite layer without functionally changing its surface topography and morphologic features. At 12 weeks, the bone-implant specimens were prepared for undecalcified thin section histologic evaluation and serial transverse sections were quantified with backscattered scanning electron microscopy for the percentage of bone apposition to the implant surface. Bone apposition averaged 3% for the polished implants and 23% for the grit-blasted implants. Bone apposition to the hydroxyapatite-coated implants averaged 74% whereas bone apposition to the titanium mask implants averaged 59%. Although there was significantly greater osseointegration with the hydroxyapatite-coated implants, 80% of the maximum bone forming response to the implant surfaces developed with the titanium mask implants. This simple, controlled experiment revealed that topography is the dominant factor governing bone apposition to hydroxyapatite-coated implants.