Fluoride release and uptake characteristics of aesthetic restorative materials.

The aims of this study were firstly to investigate the fluoride-releasing characteristics of two composite resins (Tetric and Valux Plus), two polyacid-modified resin composites (Compoglass and Dyract), and conventional glass-ionomer cement (Ceramfil beta). The second aim was to assess the fluoride uptake and subsequent release from the same range of materials. Fifteen discs (6 mm diameter and 1.5 mm height) were prepared for each material. Each disc was immersed in 4 ML of deionized water within a plastic vial. The release of fluoride was measured daily at 1, 2, 3, 4, 5, 15, 30 and 60 days. After daily fluoride release was measured for 60 days, samples were refluoridated in 1000-ppm sodium fluoride (NaF) solutions (pH 6.6) for 10 min and fluoride release was measured daily for a total of 5 days. The release of fluoride from aesthetic restorative materials was measured by using specific fluoride electrode and an ionanalyser. Results were statistically analysed by two-way repeated measure ANOVA and Duncan's multiple range test. The results revealed that all fluoride-containing materials (Ceramfil beta, Compoglass, Dyract, Tetric) released fluoride initially and the release was greatest at the first day. At any time during the test period Ceramfil beta released the most and Valux Plus did not release any detectable fluoride (P < 0.01). Sample exposures to 1000 ppm NaF solution increased the 24-h fluoride release from all fluoride-containing materials. This difference lasted only 24-48 h after exposure. Ceramfil beta had a tendency to recharge not seen with the other materials (P < 0.05).