PURPOSE: To investigate the microleakage of four hydrophilic adhesive systems: one "multiple-bottles" (Scotchbond Multi-Purpose Plus); two "one-bottle" (Single Bond, Stae); and one self-etching (Etch & Prime 3.0). MATERIALS AND METHODS: 120 bovine incisor teeth were divided into four groups (n = 30) and Class V cavities were prepared at the cemento-enamel junction. The cavities were restored with the adhesive systems and with Z100 composite. The teeth were thermocycled 1,000 times between 5+/-2 degrees C and 55+/-2 degrees C with a dwell time of 1 min, and then placed in a 2% methylene blue dye (pH 7.0) for 4 hrs, washed and sectioned vertically through the center of the restorations. The qualitative evaluation was made by three examiners who distributed pre-established scores (0-4) for each tooth using a stereomicroscope at x30 magnification. RESULTS: In enamel margins little microleakage was observed and the Kruskal-Wallis analysis did not show differences. In dentin margins the Kruskal-Wallis and multiple comparison analyses were applied: microleakage was significantly greater with Stae (median 3) and Scotchbond MP Plus (median 4). Single Bond (median 1) and Etch & Prime 3.0 (median 2) showed the best results in dentin margins, and the statistical analysis did not demonstrate differences in microleakage among these groups.
PURPOSE: To investigate the microleakage of four hydrophilic adhesive systems: one "multiple-bottles" (Scotchbond Multi-Purpose Plus); two "one-bottle" (Single Bond, Stae); and one self-etching (Etch & Prime 3.0). MATERIALS AND METHODS: 120 bovine incisor teeth were divided into four groups (n = 30) and Class V cavities were prepared at the cemento-enamel junction. The cavities were restored with the adhesive systems and with Z100 composite. The teeth were thermocycled 1,000 times between 5+/-2 degrees C and 55+/-2 degrees C with a dwell time of 1 min, and then placed in a 2% methylene blue dye (pH 7.0) for 4 hrs, washed and sectioned vertically through the center of the restorations. The qualitative evaluation was made by three examiners who distributed pre-established scores (0-4) for each tooth using a stereomicroscope at x30 magnification. RESULTS: In enamel margins little microleakage was observed and the Kruskal-Wallis analysis did not show differences. In dentin margins the Kruskal-Wallis and multiple comparison analyses were applied: microleakage was significantly greater with Stae (median 3) and Scotchbond MP Plus (median 4). Single Bond (median 1) and Etch & Prime 3.0 (median 2) showed the best results in dentin margins, and the statistical analysis did not demonstrate differences in microleakage among these groups.
Authors: Mohammed A Alqarni; Khalid M Abdelaziz; Omar Saeed Al Shahrani; Ahmed Abdullah Al Asmari; Saad Ali Sabrah; Mohammed Thamer Al Qahtani Journal: Open Access Maced J Med Sci Date: 2019-10-11