OBJECTIVE: The objective of this study was to investigate the microtensile bond strength (microTBS) of contemporary glass ionomer cements (GIC) to sound coronal dentin. METHODS: Three specimen teeth were prepared for each material tested: Fuji IX GP (GC), ChemFlex (Dentsply) and Ketac-Molar Aplicap (ESPE). GIC buildups were made according to the manufacturers' instructions. After being stored at 37 degrees C, 100% humidity for 24h, the teeth were vertically sectioned into 1x1mm beams for microTBS evaluation. Representative fractured beams were prepared for scanning (SEM) and transmission electron microscopic (TEM) examination. RESULTS: Results of the microTBS test were: Fuji IX GP (12.4+/-8.6MPa), ChemFlex (15.0+/-9.3MPa) and Ketac-Molar Aplicap (11.4+/-7.7MPa). One-way ANOVA and a multiple comparison test showed that ChemFlex had a statistically higher microTBS (p<0.05). SEM fractographic analysis showed that the predominant failure modes were interfacial and mixed failures. The GIC side of the fractured beams revealed dehydration cracks, a high level of porosity, and voids with an eggshell-like crust. TEM analysis of the demineralized dentin sides of the fractured beams revealed the presence of an intermediate layer along the GIC-dentin interface. This zone was present on the fractured dentin surface in the case of interfacial failure, and beneath GIC remnants in specimens that exhibited a mixed failure mode. SIGNIFICANCE: The findings suggest that the bonding of GIC to dentin is not weak and that the microTBS values probably represent the weak yield strengths of GICs under tension.
OBJECTIVE: The objective of this study was to investigate the microtensile bond strength (microTBS) of contemporary glass ionomer cements (GIC) to sound coronal dentin. METHODS: Three specimen teeth were prepared for each material tested: Fuji IX GP (GC), ChemFlex (Dentsply) and Ketac-Molar Aplicap (ESPE). GIC buildups were made according to the manufacturers' instructions. After being stored at 37 degrees C, 100% humidity for 24h, the teeth were vertically sectioned into 1x1mm beams for microTBS evaluation. Representative fractured beams were prepared for scanning (SEM) and transmission electron microscopic (TEM) examination. RESULTS: Results of the microTBS test were: Fuji IX GP (12.4+/-8.6MPa), ChemFlex (15.0+/-9.3MPa) and Ketac-Molar Aplicap (11.4+/-7.7MPa). One-way ANOVA and a multiple comparison test showed that ChemFlex had a statistically higher microTBS (p<0.05). SEM fractographic analysis showed that the predominant failure modes were interfacial and mixed failures. The GIC side of the fractured beams revealed dehydration cracks, a high level of porosity, and voids with an eggshell-like crust. TEM analysis of the demineralized dentin sides of the fractured beams revealed the presence of an intermediate layer along the GIC-dentin interface. This zone was present on the fractured dentin surface in the case of interfacial failure, and beneath GIC remnants in specimens that exhibited a mixed failure mode. SIGNIFICANCE: The findings suggest that the bonding of GIC to dentin is not weak and that the microTBS values probably represent the weak yield strengths of GICs under tension.
Authors: Beata Czarnecka; Patricia Deregowska-Nosowicz; Honorata Limanowska-Shaw; John W Nicholson Journal: J Mater Sci Mater Med Date: 2007-01-04 Impact factor: 4.727