Solubility and sorption of resin-based luting cements.

This study compared the seven-day water sorption, water solubility and lactic acid solubility of three composite cements and three resin-modified glass-ionomer cements. Disc-shaped specimens measuring 15 mm x 0.5 mm were prepared according to each manufacturer's specifications and desiccated to a constant mass. Specimens were then placed in distilled water at 37 degrees C for seven days. Acid solubility was performed in 0.01 M lactic acid. The weight changes of the specimens after immersion in distilled water or 0.01 M lactic acid were measured using an electronic analytical balance. A one-way ANOVA followed by the Ryan-Einot-Gabriel-Welsch (REGW) multiple range test was performed on all data. Significant differences (p < 0.05) were found among several cements tested for each of the properties investigated. Due to their hydrophilic nature, all resin-modified glass-ionomer cements showed significantly higher water sorption compared to composite cements.