OBJECTIVE: In the present study, the authors evaluated tensile bond strength of composite resin to dentin treated with Nd:YAG laser before and after bonding procedures. SUMMARY BACKGROUND DATA: Lasers have been widely used in dentistry and have contributed to the development of new technologies. Adhesive systems have been indicated for most dental procedures and have produced good results. Studies concerned with the combined use of this adhesive system was the subject of this study. METHODS: Thirty noncarious human anterior teeth, freshly extracted, for periodontal reasons, were used. After grinding the buccal dentinal surface until its exposition, specimens were separated into three groups and received the following treatments: (group 1) control--acid etching plus primer plus bond; (group 2) laser plus acid etching plus primer plus bond; (group 3) acid etching plus primer plus bond plus laser. Specimens of composite resin (Z100, 3M, Saint Paul, MN) were constructed on an inverted truncated 3-mm diameter cone mold. Tensile bond strength was performed using Inströn Universal machine, at 0.5 mm/min speed. RESULTS: Analysis of variance (ANOVA) (p < 0.05) determined that the type of dentinal treatments used had an influence on tensile bond strength. Tukey's test, however, showed that group 1 (15.46) and 3 (15.67) had similar results both of which were higher than group 2 (4.57). CONCLUSIONS: Based on the results obtained, one can conclude that group 1 (without laser) and group 3 (laser after bonding) had similar results, both higher than those observed for group 2 (laser before bonding). These results indicate that more research is needed about how a hybrid layer is formed when laser radiation is used.
OBJECTIVE: In the present study, the authors evaluated tensile bond strength of composite resin to dentin treated with Nd:YAG laser before and after bonding procedures. SUMMARY BACKGROUND DATA: Lasers have been widely used in dentistry and have contributed to the development of new technologies. Adhesive systems have been indicated for most dental procedures and have produced good results. Studies concerned with the combined use of this adhesive system was the subject of this study. METHODS: Thirty noncarious human anterior teeth, freshly extracted, for periodontal reasons, were used. After grinding the buccal dentinal surface until its exposition, specimens were separated into three groups and received the following treatments: (group 1) control--acid etching plus primer plus bond; (group 2) laser plus acid etching plus primer plus bond; (group 3) acid etching plus primer plus bond plus laser. Specimens of composite resin (Z100, 3M, Saint Paul, MN) were constructed on an inverted truncated 3-mm diameter cone mold. Tensile bond strength was performed using Inströn Universal machine, at 0.5 mm/min speed. RESULTS: Analysis of variance (ANOVA) (p < 0.05) determined that the type of dentinal treatments used had an influence on tensile bond strength. Tukey's test, however, showed that group 1 (15.46) and 3 (15.67) had similar results both of which were higher than group 2 (4.57). CONCLUSIONS: Based on the results obtained, one can conclude that group 1 (without laser) and group 3 (laser after bonding) had similar results, both higher than those observed for group 2 (laser before bonding). These results indicate that more research is needed about how a hybrid layer is formed when laser radiation is used.
Authors: T M Silva; L L Gonçalves; B M Fonseca; S R M S Esteves; D C Barcellos; A J Damião; S E P Gonçalves Journal: Lasers Med Sci Date: 2015-10-28 Impact factor: 3.161