Vibrational spectroscopy of formamide-intercalated kaolinites.

The vibrational spectroscopy of low and high defect kaolinites fully and partially intercalated with formamide have been determined using a combination of X-ray diffraction, DRIFT and Raman spectroscopy. Expansion of the high defect kaolinite to 10.09 A resulted in a decrease in the peak width of the d(001) peak attributed to a decrease in defect structures upon intercalation. Changes in the defect structures of the low defect kaolinite were observed. Additional infrared bands were observed for the formamide intercalated kaolinites at 3629 and 3606 cm(-1). The 3629 cm(-1) band is attributed to the hydroxyl stretching frequency of the inner surface hydroxyl group hydrogen bonded to the carboxyl group of the formamide. The 3606 cm(-1) band is ascribed to water in the interlayer. Concomitant changes are observed in both the hydroxyl deformation modes and in the carboxyl bands.