Photocatalytic TiO(2) deposition by chemical vapor deposition.

Dip-coating, spray-coating or spin-coating methods for crystalline thin film deposition require post-annealing process at high temperature. Since chemical vapor deposition (CVD) process is capable of depositing high-quality thin films without post-annealing process for crystallization, CVD method was employed for the deposition of TiO(2) films on window glass substrates. Post-annealing at high temperature required for other deposition methods causes sodium ion diffusion into TiO(2) film from window glass, resulting in the degradation of photocatalytic efficiency. Anatase-structured TiO(2) thin films were deposited on window glass by CVD, and the photocatalytic dissociation rates of benzene with CVD-grown TiO(2) under UV exposure were characterized. As the TiO(2) film deposition temperature was increased, the (112)-preferred orientations were observed in the film. The (112)-preferred orientation of TiO(2) thin film resulted in a columnar structure with a larger surface area for benzene dissociation. Obviously, benzene dissociation rate was maximum when the degree of the (112) preferential orientation was maximum. It is clear that the thin film TiO(2) should be controlled to exhibit the preferred orientation for the optimum photocatalytic reaction rate. CVD method is an alternative for the deposition of photocatalytic TiO(2).