Poly(ethylene oxide)-poly(propylene oxide)-poly(ethylene oxide)/poly(epsilon-caprolactone) (PCL) amphiphilic block copolymeric nanospheres. II. Thermo-responsive drug release behaviors.

Amphiphilic block copolymers composed of relatively hydrophilic PEO-PPO-PEO block copolymer (Pluronic) and poly (epsilon-caprolactone) with hydrophobic character were synthesized by ring-opening polymerization of epsilon-caprolactone in the presence of PEO-PPO-PEO block copolymer using stannous octoate as a catalyst. Pluronic/PCL block copolymeric nanospheres with core-shell structure were prepared by dialysis method. They showed the average diameter of 116-196 nm depending on the type of copolymer. All the nanosphere samples exhibited a narrow size distribution. The critical micelle concentrations of Pluronic/PCL amphiphilic block copolymers determined by fluorescence spectroscopy were lower than that of the common low molecular weight surfactant. Their core-shell structure was confirmed by 1H NMR spectroscopy. Pluronic/PCL block copolymeric nanospheres exhibited the reversible change of size depending on the temperature. Release behaviors of indomethacin from Pluronic/PCL block copolymeric nanospheres also showed temperature dependence and a sustained release pattern. In addition, cytotoxicity test using an MTT assay method revealed that these indomethacin-loaded Pluronic/PCL nanospheres could remarkably reduce the cell damage compared with the unloaded free indomethacin.